Vitrebond Plus liner/base can be used with any type of adhesive (light or self cured; separate etch or self-etch, i.e. - 4th, 5th or 6th generation adhesives) on dentin or enamel.
How do you use Vitrebond liner?
Apply the mixed liner/base to the dentin surfaces of the prepared cavity in a thin layer (1/2mm or less) using a ball applicator or other suitable instrument. The Vitrebond liner/base has a minimum working time of 2 minutes 40 seconds at room temperature. Higher temperatures will shorten working time.
Is Vitrebond radiopaque?
The glass ionomer cements were substantially less radiopaque than other materials. ... Of the three resin-modified glass ionomer materials, Vitrebond was the most radiopaque and Fuji Lining LC was the least radiopaque.
When should I use Vitrebond?
its composition and curing mechanism extensively described in the literature. It is recommend for use as a liner or base under composite, amalgam, metal and ceramic restorations. Vitrebond Liner/Base is not indicated for direct pulp capping.
Do you etch before or after liner?
If an RMGI base or liner is to be used, it should be placed and cured before the etching or adhesive steps. For details regarding specifics of adhesive systems, refer to Chapter 40. The preparation should be etched for 15 to 20 seconds with an acid gel.
What is a indirect pulp cap?
An indirect pulp cap is a procedure that protects a compromised tooth without exposed pulp. It may help you avoid more invasive procedures like tooth extraction or a root canal. It retains the tooth and allows its roots to continue developing.Jun 10, 2021
What is Vitrebond?
Vitrebond™ is a light-cured, resin-modified glass ionomer (RMGI) liner/base material. It is recommended for use as a liner or base under composite, amalgam, metal and ceramic restorations. It is not indicated for direct pulp capping. Excellent bond strength with a hard set in seconds.
What is Vitrebond made of?
General Information Vitrebond™ light cure glass ionomer liner/base, manufactured by 3M™ ESPE™, is comprised of a powder and a liquid component. The powder component is a light sensitive fluoro-aluminosilicate glass. The liquid component is a light sensitive polyalkenoic acid.
What is the difference between direct pulp capping and indirect pulp capping?
Two different types of pulp cap are distinguished. In direct pulp capping, the protective dressing is placed directly over an exposed pulp; and in indirect pulp capping, a thin layer of softened dentin, that if removed would expose the pulp, is left in place and the protective dressing is placed on top.
Is glass ionomer radiolucent?
Glass ionomer cements have been used for many clinical situations, such as restorations in deciduous teeth, base or liner material for internal reconstruction and even as material for retrograde radicular restoring. However, the first glass ionomer cements were radiolucent, fact that hindered its use on clinics [21].
What is Vitrebond for?
Vitrebond™ is a light-cured, resin-modified glass ionomer (RMGI) liner/base material. It is recommended for use as a liner or base under composite, amalgam, metal and ceramic restorations.